Inner hole laser cladding equipment (workpiece inner surface repair system)

get started

Presentation of the equipment's characteristics

The inner hole laser cladding equipment (workpiece inner surface repair system) has the advantages of high integration, high precision and high adaptability. It can easily realize efficient and high-quality laser processing of the inner surfaces of different types of parts. It has accessibility that is difficult to obtain with traditional optical heads. Combined with our company’s existing ultra-high-speed laser cladding technology, it can complete high-speed cladding processing of products such as cylinders and columns.

processed samples
  1. Concentrated heat, small heat input, small heat-affected zone, no effect on organizational changes;
  2. Smooth cladding surface, less machining;
  3. Shallow fusion depth, low cladding layer dilution, good anti-corrosion effect;
  4. Suitable for cladding of various materials, low cladding cost;
  5. The equipment has the advantages of high integration, high precision and high adaptability;
Equipment NameInner Hole Laser Cladding Equipment
Power500-4000W
Rotation Speed0-150RPM
Powder Particle Size25-150μm
Cladding Thickness0.30-0.65mm
Powder Feeding Rate0.1-200g/min
Efficiency0.5m²/h

Inner hole cladding test

1.The inner wall of the cylinder liner is laser clad, the thickness of the cladding layer is 0.3-0.6mm on one side, the surface of the cladding layer is continuous and uniform, and no pore defects are found.

Cylinder liner processing diagramPenetrant testing of the inner hole cladding layer showed no crack defectsPenetration test diagram
  1. Cut the cladding layer along the vertical cladding scanning direction to prepare the metallographic sample. Use the 100x lens of the metallographic microscope to observe the bonding between the cladding layer and the substrate and the internal quality of the cladding layer. The cladding layer and the substrate are metallurgically bonded, the melting depth is shallow, and there is no unfused and pore defects inside the cladding layer. The thickness of the cladding layer is about 0.3mm.
  2. Grind the cladding parts, and keep the thickness of the cladding layer at about 0.15mm, with a surface roughness of Ra0.8. According to the GB/T10125-1997 standard, the neutral salt spray corrosion test is carried out. After 100h of continuous spraying, the surface rust of the cladding layer is observed, and no rust spots are found on the surface of the cladding layer.
  3. Use a portable hardness tester to test the hardness of the cladding layer after grinding. Take 6 points evenly along the circumference of the experimental tube. The hardness range of the cladding layer is about 50-53HRC.
Metallographic diagramSalt spray test chart